| Sample | Static Time 500 To 500V | Decay from 0V To 100V | Surface Resistivity 50% humidity (Q/sq) | Surface Resistivity 15% humidity (Q/sq) | Resistance to Ground («) | Volume Resistivity (Qcm) | Solvent Resist, (sfc. res. after IPA & acetone) | 85/85 Test (sfc. res. after 100 hours at 85% humidity & 85°C) | Contamination Nonvolatile Residue (rag/ft2) |
| VPI Conductile Con 2 Floor Tile (as installed) | 0.01 s | 0.01 s | 5.5x lO5 | 8.9 xlO5 | 2.6 x l05 | 7xl06 |
Pass |
Pass | 19.5 |
|
VPI Conductile LE
(as installed) |
0.01 s | 0.01 s | 4.7 x l05 | 8.8 x 105 | 2.5 x lO5 | 6x106 |
Pass |
Pass |
3. 47 |
|
VPI Conductile
XLE
(as installed) |
0.01 s | 0.01 s | 4.3 x lO5 | 6.9 x lO5 | 3.8 x lO5 | 2xl06 |
Pass |
Pass |
1. 31 |
| Flexco Dissipative Floor Tile | 0.01 s | 0.01 s | 2.3xl06 | 2.1xl08 | 2xl06 | 2x10'° | Pass | Pass | 19. 7 |
| ForboColorex 5201 Floor Tile | 0.01 s | 0.01 s | 8xl08 | IxlO9 | 5xl06 | 10'° | Pass | Pass | 29. 8 |
| Datwyler 6090 Unifloor Mat | 0.01 s | 0.01 s | IxlO8 | IxlO9 | 3xl06 | 3xl08 | Pass | Pass but color faded | 21 . 79 |
| Westek Decade 5300 Mat | 0.01 s | 0.01 s | 1.9xl06 | 7.5xl07 | 1.2xl06 | <105 | Pass | Pass | 26 . 4 |
| TekStil6015 Conductive Unifloor Mat | 0.01 s | 0.01 s | 7.5xl08 | IxlO9 | 3xl06 | 6xl07 | Pass | Pass but color faded |
23.89 |
| Tek Stil 7294 Static Dissipative Unifloor Mat | 0.01 s | 0.02s | 5. IxlO8 | IxlO9 | 3xl06 | 6xl07 | N/a | Pass | 24 .3 |
| Ergomat Gray Polyethylene | 0.03s | 0.1 s | 2xl010 | 9x10'° | IxlO8 | 4xl09 | N/a | Fail — crumbled | 21. 6 |
| Clean ESD Blue Polyethylene Mat | 0.01 s | 0.08s | 2x1 09 | 2xl09 | 7xl07 | 8xl09 | N/a | Pass | 53. 8 |
| Norament 928 al S grano (as installed) | N/a | N/a | N/a | N/a | 2x1 0s | N/a | N/a | Pass | N/a |
| Noraplan mega al rubber (as installed) | N/a | N/a | N/a | N/a | IxlO8 | N/a | N/a | Pass | N/a |
| 3M 8414 Dissipative Blue | 0.01 s | 0.01 s | 6xl07 | IxlO8 | IxlO9 | N/a | N/a | N/a | N/a |
| Clean Zone Static Dissipative Mat (blue side) | 0.02s | 0.18s | 4xl09 | 4xl09 | IxlO9 | 2xl010 | N/a | N/a | 68. 3 |